Semiconductor Device and Method

ABSTRACT

A transistor based on topological insulators is provided. In an embodiment a topological insulator is used to form both the channel as well as the source/drain regions, wherein the channel has a first thickness such that the topological insulator material has properties of a semiconductor material and the source/drain regions have a second thickness such that the topological insulator has properties of a conductive material.

PRIORITY CLAIM AND CROSS-REFERENCE

This application claims priority to and the benefit of U.S. Provisional Application No. 62/273,628, filed on Dec. 31, 2015, entitled “Tunable Gap Ultra-Thin-Body Transistor Based on a Topological Insulator,” which application is hereby incorporated herein by reference in its entirety.

BACKGROUND

Semiconductor devices are used in a variety of electronic applications, such as personal computers, cell phones, digital cameras, and other electronic equipment, as examples. Semiconductor devices are typically fabricated by sequentially depositing insulating or dielectric layers, conductive layers, and semiconductive layers of material over a semiconductor substrate, and patterning the various material layers using lithography to form circuit components and elements thereon.

Transistors are circuit components or elements that are often formed on semiconductor devices. Many transistors may be formed on a semiconductor device in addition to capacitors, inductors, resistors, diodes, conductive lines, or other elements, depending on the circuit design. Improvements in transistor designs are desired.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 illustrates a formation of a channel layer, a gate dielectric layer, and a gate electrode layer in accordance with some embodiments.

FIGS. 2A-2C illustrate band gaps of topological insulators in accordance with some embodiments.

FIG. 3 illustrates a patterning of the channel layer, the gate dielectric layer, and the gate electrode layer in accordance with some embodiments.

FIGS. 4A-4B illustrate a formation of source/drain regions in accordance with some embodiments.

FIGS. 5A-5C illustrate a formation of the channel and source/drain regions in accordance with some embodiments.

FIGS. 6A-6B illustrate a formation of the channel on the gate dielectric in accordance with some embodiments.

FIG. 7 illustrates a formation of a second channel layer, a second gate dielectric layer, and a second gate electrode in accordance with some embodiments.

FIGS. 8A-8B illustrate a formation of source/drain regions in accordance with some embodiments.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the invention. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

Embodiments will now be described with respect to a tunable gap ultra-thin body transistor which is based on a topological insulator. However, the embodiments described herein may be applied in any suitable application.

With reference now to FIG. 1, there is illustrated a substrate 101, a first channel layer 103, a first gate dielectric layer 105, and a first gate electrode layer 107. In an embodiment the substrate 101 may comprise bulk silicon, doped or undoped, or an active layer of a silicon-on-insulator (SOI) substrate. Generally, an SOI substrate comprises a layer of a semiconductor material such as silicon, germanium, silicon germanium, SOI, silicon germanium on insulator (SGOI), or combinations thereof. Other substrates that may be used include sapphire, multi-layered substrates, gradient substrates, or hybrid orientation substrates. Any suitable substrate may be utilized.

The first channel layer 103 may be formed over the substrate 101 and will be used to form a first channel 305 (not illustrated in FIG. 1 but illustrated and discussed below with respect to FIG. 3) for a single-gate transistor 400 (also not illustrated in FIG. 1 as being completed but illustrated and described below with respect to FIG. 4A). In an embodiment the first channel layer 103 may be a topological insulator material wherein the material has a bulk structure with an insulating or semiconducting (gapped) structure as well as conducting (gapless) edges or surfaces due to non-trivial topology of a band structure caused by interactions between spin and orbital degrees of freedom. In particular embodiments in which the first channel layer 103 is a topological insulating material, the first channel layer 103 may be a material such as Bi₂Se₃, Bi₂Te₃, Sb₂Te₃, or tetradymite-like ternary compounds with a structure such as M₂X₂Y such as Bi₂Te₂Se, Bi₂Te₂S, Bi₂Se₂S, Sb₂Te₂Se, Sb₂Te₂S, or the like. However, any suitable topological insulator may be utilized.

Additionally, with respect to the materials utilized for the first channel layer 103, the material of the first channel layer 103 will have a critical thickness T_(c), wherein the thickness of the material of the first channel layer 103 will determine the properties of the material of the first channel layer 103 and the properties of the material for the first channel layer 103 will change as the thickness of the material for the first channel layer 103 changes. For example, in a particular embodiment in which Bi₂Se₃ is utilized as the material for the first channel layer 103, the Bi₂Se₃ will have a critical thickness of six quintuple layers (e.g., layers of Se—Bi—Se—Bi—Se), below which the Bi₂Se₃ will have properties of a semiconductor material and above which the Bi₂Se₃ will have properties of a topological insulator which has bulk insulator properties along with conductive surface states.

FIG. 2A helps to illustrate this change and separation of properties based upon thicknesses. When the thickness of a Bi₂Se₃ film is reduced to several nanometres, the surface-state wavefunctions from the two surfaces of Bi₂Se₃ film are interfered and overlapped. Therefore, a gap opens and no surface state exists. As illustrated in FIG. 2A, a single quintuple layer (1QL) of Bi₂Se₃ has an energy band gap that does not allow for the conduction of electricity and causes the Bi₂Se₃ to have the properties of a semiconductor material. However, as illustrated in FIG. 2B, as the number of layers of Bi₂Se₃ increases, the surface states can very well exist when the critical thickness of Bi₂Se₃ has been reached (which for Bi₂Se₃ is about 6 quintuple layers), the band gap is bridged, and the Bi₂Se₃ will have the properties of a topological insulator, such that the material is an insulator but which has conductive surface states such that electricity will flow along the surface of the topological insulator. As such, the thickness of the material utilized for the first channel layer 103 determines its properties, and control of this thickness will also control the properties that are obtained from the formation of the first channel layer 103.

FIG. 2C helps to illustrate this change in properties based upon the thickness of the material of the first channel layer 103 in another fashion. In particular, FIG. 2C illustrates the bandgap of each number of quintuple layers from 1 quintuple layer of Bi₂Se₃ to 7 quintuple layers of Bi₂Se₃ and illustrates that at 6 quintuple layers the bandgap reaches zero and the Bi₂Se₃ has the properties of a topological insulator with metallic surface states that allows for the flow of electricity. However, below 6 quintuple layers, there is a non-zero bandgap which causes the Bi₂Se₃ to have the properties of a semiconductor material.

In order to function appropriately as the first channel 305, the first channel layer 103 is formed to have a first thickness T₁ that is below the critical thickness T_(c) (shown in relative located in FIG. 1) of the material used for the first channel layer 103. In a particular embodiment in which the first channel layer 103 is Bi₂Se₃, Bi₂Te₃, or Sb₂Te₃, the first channel layer 103 is formed to have a thickness of less than 6 quintuple layers, such as having a thickness of 1 quintuple layer, or about 1 nm. However, any suitable thickness may be utilized depending upon the properties of the topological insulator material being utilized. By forming the first channel layer 103 to have the first thickness T₁ below the critical thickness T_(c) of the material chosen for the first channel layer 103, the first channel layer 103 will have a material with semiconductor properties and not conductive properties.

The first channel layer 103 may be formed using a process such as an epitaxial growth process. In a particular embodiment in which the first channel layer 103 is formed from a material such as Bi₂Se₃, the epitaxial growth process may proceed at a temperature of between about 100° C. and about 500° C., and at a pressure less than about 2.0×10⁻⁹ Torr, using any suitable source or sources for bismuth and selenium, such as evaporated high-purity Bi (99.99%) and Se (99.99%). However, any suitable growth or deposition process, such as an atomic layer deposition process or the like, may also be used.

Additionally, the epitaxial growth process may be continued for a time that is sufficient to grow the first channel layer 103 to the first thickness T₁ without growing the first channel layer 103 to a thickness greater than the critical thickness T_(c). In an embodiment in which the deposition rate of Bi₂Se₃ films is about 0.67 angstrom/min, the epitaxial growth process may be performed for a first time of between about 70 sec and about 270 sec. However, any suitable time may be utilized.

Once the first channel layer 103 has been formed, a first gate dielectric layer 105 and a first gate electrode layer 107 may be formed over the first channel layer 103. The first gate dielectric layer 105 may be formed from a high permittivity (high-k) material (e.g., with a relative permittivity greater than about 5) such as aluminum oxide (Al₂O₃), hafnium oxide (HfO₂), hafnium oxynitride (HfON), lanthanum oxide (La₂O₃), or zirconium oxide (ZrO₂), or combinations thereof, with an equivalent oxide thickness of about 0.5 nm to about 2 nm. Additionally, any combination of silicon dioxide, silicon oxynitride, and/or high-k materials may also be used for the first gate dielectric layer 105. The first gate dielectric layer 105 may be formed using a process such as atomic layer deposition, chemical vapor deposition, sputtering, or the like.

The first gate electrode layer 107 may comprise a conductive material and may be selected from a group comprising of gold, titanium, platinum, aluminum, polycrystalline-silicon (poly-Si), poly-crystalline silicon-germanium (poly-SiGe), metallic nitrides, metallic silicides, metallic oxides, and metals. Examples of metallic nitrides include tungsten nitride, molybdenum nitride, titanium nitride, and tantalum nitride, or their combinations. Examples of metallic silicide include tungsten silicide, titanium silicide, cobalt silicide, nickel silicide, platinum silicide, erbium silicide, or their combinations. Examples of metallic oxides include ruthenium oxide, indium tin oxide, or their combinations. Examples of other metals that may be used include tantalum, tungsten, copper, molybdenum, nickel, etc. Any suitable material may be used to form the first gate electrode layer 107.

The first gate electrode layer 107 may be deposited by sputter deposition, chemical vapor deposition (CVD), or other techniques known and used in the art for depositing conductive materials. The thickness of the first gate electrode layer 107 may be in the range of about 200 angstroms to about 4,000 angstroms. Dopants may or may not be introduced into the first gate electrode layer 107 at this point. Dopants may be introduced, for example, by molecular doping techniques thru charge transfer.

FIG. 3 illustrates that, once the first gate electrode layer 107 has been formed, the first gate electrode layer 107 may be patterned to form a first gate electrode 301. The first gate electrode 301 may be formed by depositing and patterning a first gate mask (not illustrated in FIG. 3) on the first gate electrode layer 107 using, for example, deposition and photolithography techniques known in the art. The first gate mask may incorporate commonly used masking materials, such as (but not limited to) photoresist material, silicon oxide, silicon oxynitride, and/or silicon nitride. Once the first gate mask has been placed, the first gate electrode layer 107 may be etched using plasma etching to form the first gate electrode 301. In an embodiment the first gate electrode layer 107 may be patterned to have a first width W₁ of between about 7 nm and about 100 μm.

FIG. 3 also illustrates a patterning of the first gate dielectric layer 105 and the first channel layer 103. In an embodiment the patterning of the first gate dielectric layer 105 and the first channel layer 103 may be initiated by removing the first gate mask using, e.g., an ashing or other removal process, and a second gate mask may be deposited and patterned. In an embodiment the second gate mask may be deposited and patterned using, for example, deposition and photolithography techniques known in the art. The second gate mask may incorporate commonly used masking materials, such as (but not limited to) photoresist material, silicon oxide, silicon oxynitride, and/or silicon nitride. Once the second gate mask has been placed, the first gate dielectric layer 105 and the first channel layer 103 may be etched using plasma etching to form the first gate dielectric 303 and the first channel 305. In an embodiment the first gate dielectric 303 and the first channel 305 may be patterned to have a second width W₂ of between about 7 nm and about 100 μm.

FIGS. 4A-4B illustrate a formation of source/drain regions 401 in contact with the first channel 305. In an embodiment the source/drain regions 401 comprises a material with a critical thickness T_(c) as described herein, wherein the properties of the material used for the source/drain regions 401 are dependent at least in part upon the thickness of the material. In some embodiments the material of the source/drain regions 401 is a topological insulator and, in particular embodiments, is the same topological insulator material as the first channel 305. For example, in an embodiment in which the first channel 305 is Bi₂Se₃, the source/drain regions 401 are also Bi₂Se₃, although any suitable material may be used.

However, while the first channel 305 is formed using a topological insulator with a thickness that keeps the properties of the topological insulator as a semiconductor material (e.g., below 6 quintuple layers for Bi₂Se₃, such as 1 quintuple layer), the source/drain regions 401 are formed using a topological insulator material with a second thickness T₂ that is greater than the critical thickness T_(c) of the material. By forming the material of the source/drain regions 401 to have the second thickness T₂ greater than the critical thickness T_(c), the material of the source/drain regions 401 will have different properties than the material of the first channel 205, such as by having the properties of a topological insulator with bulk insulating properties as well as having surfaces with metallic behavior that allows for the conduction of electricity along the surface. In particular embodiments in which Bi₂Se₃, Bi₂Te₃, or Sb₂Te₃ are utilized for the source/drain regions 401, the source/drain regions 401 may be formed with the second thickness T₂ of six quintuple layers or greater, such as about 6 nm or greater. The source/drain regions 401 may be formed to have a third width W₃ of between about 7 nm and about 100 μm.

In an embodiment the source/drain regions 401 may be formed from similar materials and using similar processes as the first channel layer 103 (described above with respect to FIG. 1). For example, the source/drain regions 401 may be formed using a process such as molecular beam epitaxial growth. However, for the process of forming the source/drain regions 401, instead of continuing the process for the first time of between about 70 sec and about 270 sec, which would result in the first thickness T₁ below the critical thickness T_(c), the epitaxial growth process for the source/drain regions 401 is continued for a second time of between about 6 min and about 120 min, such that the source/drain regions 401 have the second thickness T₂ greater than the critical thickness T_(c). However, any suitable process may be utilized to form the source/drain regions 401.

FIG. 4B illustrates a top-down view of the single-gate transistor 400. As can be seen, the first gate dielectric 303 may be formed to have a first length L₁ of between about 7 nm and about 100 μm. Additionally, the source/drain regions 401 may be formed to have a second length L₂ of between about 7 nm and about 100 μm. The first gate electrode 301 may be formed to have a third length L₃ of between about 7 nm and about 100 μm. However, any suitable dimensions may be utilized.

By forming the first channel 305 to have the first thickness T₁ such that the first channel 305 has the properties of a semiconductor material and by also forming the source/drain regions 401 to have the second thickness T₂ such that the source/drain regions 401 have the properties of a topological insulator with a conductive surface, the same material (e.g., Bi₂Se₃) can be used for both the first channel 305 as well as the source/drain regions 401 such that there is no lattice mismatch between the first channel 305 and the source/drain regions 401. As such, the overall process may be simplified while taking advantage of the properties of the topological insulators in the formation of transistors. For example, by forming the single-gate transistor 400 with the first channel 305 and the source/drain regions 401 as described above, a normally-off topological insulator based transistor with a low contact resistance may be obtained. Additionally, because materials such as Bi₂Se₃ have a layered crystal structure consisting of stacked Se—Bi—Se—Bi—Se quintuple layers (QLs), and since the channel thickness in some embodiments is nearly 1 QL, the short channel effects in devices that utilized these embodiments is the same as FETs based on two-dimensional materials. In other words, short-channel effects can be suppressed by reducing the gate dielectric thickness, which enhances the electrostatic control from the gate.

FIGS. 5A-5C illustrate an embodiment of a process that may be used to manufacture a second single-gate transistor 500 using, e.g., a topological insulator. In this embodiment the first channel layer 103 is formed on the substrate 101 as described above with respect to FIG. 1 (e.g., an epitaxial growth process). In this embodiment, however, the first channel layer 103 is initially grown to the second thickness T₂ which is larger than the critical thickness T_(c) of the material chosen for the first channel layer 103. As such, the first channel layer 103 in this embodiment is initially formed with the properties of the topological insulator, with both the bulk insulator along with the conductive surface.

FIG. 5B illustrates that, once the first channel layer 103 has been grown to the second thickness T₂, the first channel 305 and the source/drain regions 401 are formed from the first channel layer 103 (with the separation between the first channel layer 103 and the source/drain regions 401 being illustrated by the dashed lines in FIG. 5B). In an embodiment the first channel 305 and the source/drain regions 401 are formed simultaneously from the first channel layer 103 (with the second thickness T₂) by patterning the first channel layer 103 and reducing the thickness of the first channel layer 103 until the first channel 305 has the first thickness T₁ below the critical thickness T_(c) such that the first channel 305 has the properties of a semiconductor material.

The thickness of the first channel layer 103 may be reduced by initially placing a source/drain mask (not separately illustrated in FIG. 5B) over those portions of the first channel layer 103 that are desired to be formed into the source/drain regions 401. In an embodiment the source/drain mask may be deposited and patterned using, for example, deposition and photolithography techniques known in the art. The source/drain mask may incorporate commonly used masking materials, such as (but not limited to) photoresist material, silicon oxide, silicon oxynitride, and/or silicon nitride. Once the source/drain mask has been placed, the exposed portions of the first channel layer 103 may be etched using plasma etching to form the first channel 305 (with the thickness reduced to below the critical thickness T_(c)) and the source/drain regions 401 (without the thickness reduced to below the critical thickness T_(c)).

FIG. 5C illustrates that, once the first channel 305 and the source/drain regions 401 have been formed from the first channel layer 103, the first gate dielectric 303 and the first gate electrode 301 may be formed over the first channel 305. In an embodiment the first gate dielectric 303 may be formed as described above with respect to FIGS. 1 and 3. For example, the first gate dielectric layer 105 (not separately illustrated in FIG. 5C) may be formed by initially forming a layer of material such as aluminum oxide or hafnium oxide using a process such as atomic layer deposition, chemical vapor deposition, sputtering, or the like. By using a conformal deposition process such as atomic layer deposition, the first gate dielectric layer 105 will take on the shape of the underlying structures, forming a “U” shape between the source/drain regions 401 and over the first channel 205.

Once the first gate dielectric layer 105 has been deposited, the first gate electrode layer 107 (not separately illustrated in FIG. 5C) may be deposited over the first gate dielectric layer 105. In an embodiment the first gate electrode layer 107 may be formed as described above with respect to FIG. 1. For example, the first gate electrode layer 107 may be deposited by depositing a conductive material such as gold, titanium, platinum, or aluminum over the dielectric material using a process such as sputtering, although any other suitable material or method of manufacture may be utilized.

Once the first gate dielectric layer 105 and the first gate electrode layer 107 have been formed, the first gate dielectric layer 105 and the first gate electrode layer 107 may be patterned into the first gate dielectric 303 and the first gate electrode 301, respectively. In an embodiment the first gate dielectric layer 105 and the first gate electrode layer 107 may be patterned as described above with respect to FIG. 3, whereby one or more photoresists are deposited, exposed, developed, and then used as mask(s) in order to pattern the first gate dielectric layer 105 and the first gate electrode layer 107 into the desired shapes. In an embodiment the first gate electrode 301 may be patterned to a fourth width W₄ of between about 7 nm and about 100 μm, and the first gate dielectric 303 may be patterned to a fifth width W₅ of between about 7 nm and about 100 μm.

FIG. 6A illustrates another embodiment in which the first channel 305 and the source/drain regions 401 are formed over the first gate electrode 301 and the first gate dielectric 303. In this embodiment the first gate electrode 301 and the first gate dielectric 303 are initially formed prior to the formation of the first channel 305 and the source/drain regions 401. In an embodiment the first gate electrode 301 and the first gate dielectric 303 may be formed as described above with respect to FIGS. 1 and 3. For example, the first gate dielectric layer 105 and the first gate electrode layer 107 may be formed by initially forming a conductive material such as gold, titanium, platinum, or aluminum over the dielectric material using a process such as sputtering and then depositing a layer of material such as aluminum oxide, hafnium oxide, or silicon oxide using a process such as atomic layer deposition. Once the first gate dielectric layer 105 and the first gate electrode layer 107 have been formed, the first gate dielectric layer 105 and the first gate electrode layer 107 may be patterned, if desired, using a suitable photolithographic masking and etching process in order to form the first gate electrode 301 and the first gate dielectric 303. However, any suitable process for depositing the first gate electrode 301 and the first gate dielectric 303 may be utilized. However, in this embodiment the first gate dielectric layer 105, if desired, may be formed to a thickness of between about 50 nm to about 500 nm, although any suitable thickness may be utilized.

Once the first gate electrode 301 and the first gate dielectric 303 have been formed, the first channel 305 and the source/drain regions 401 may be formed over the first gate dielectric 303. In an embodiment the first channel 305 and the source/drain regions 401 may be formed as described above with respect to FIGS. 1-5B. For example, the first channel 205 and the source/drain regions 401 may be formed by initially growing the first channel layer 103 to the second thickness T₂ such that the material of the first channel layer 103 has the properties of a topological insulator (with metallic conducting surface states), and then reducing the thickness of a portion of the original first channel layer 103 to the first thickness T₁ in order to form the first channel 305 with properties of a semiconductor (as described above with respect to FIGS. 5A-5B). As such, the first gate dielectric 303 has a planar surface facing the first channel 305 and the source/drain region 401 is in physical contact that planar surface.

In another embodiment similar to the embodiment described above with respect to FIGS. 1-4B, the first channel layer 103 may be grown on the first gate dielectric 303 to the first thickness T₁ and without growing to a thickness greater than the critical thickness T_(c). As such, the first channel layer 103 is formed to have properties of a semiconductor material. Once the first channel layer 103 has been grown to the first thickness T₁, the first channel layer 103 may be patterned into the first channel 305 by placing, exposing, and developing a photoresist (not separately illustrated in FIG. 6A) over the first channel layer 103 before using the photoresist as a mask during an etching process such as a dry etch to form the first channel 305.

In addition to forming the first channel 305, the etching process will also expose the underlying first gate dielectric 303. Once the underlying first gate dielectric 303 has been exposed, the source/drain regions 401 may be formed on opposite sides of the first channel 305 as described above with respect to FIG. 4A. For example, the source/drain regions 401 may be formed from the same material as the first channel 305 using an epitaxial growth process to epitaxially grow the source/drain regions 401 onto the first gate dielectric 303. Additionally, the source/drain regions 401, while being grown from the same material as the first channel 305, will grow the source/drain regions 401 to have the second thickness T₂ greater than the critical thickness T_(c) such that the source/drain regions 401 will have the properties of a topological insulator with metallic surface states. For example, in an embodiment in which the source/drain regions 401 are Bi₂Se₃, the source/drain regions 401 will be grown to a thickness that is greater than six quintuple layers. However, any suitable thickness may be utilized. As such, the first gate dielectric 303 in this embodiment has a first planar surface facing the first channel 305 and a second planar surface perpendicular to the first planar surface, wherein the source/drain region 401 is in physical contact the second planar surface.

FIG. 6B illustrates a top-down view of the structure of FIG. 6A. In this view, it can be seen that the first channel 305 is over the first gate dielectric 303 and extends between the source/drain regions 401. In an embodiment the first channel 305 in this structure has a fourth length L₄ of between about 7 nm and about 100 μm, while the source/drain regions 401 have a fifth length L₅ of between about 7 nm and about 100 μm. However, any suitable dimensions may be utilized.

By forming the first channel 305 and the source/drain regions 401 over the first gate dielectric 303, additional flexibility in the manufacturing process may be obtained. Such flexibility allows manufacturers the ability to modify their processes to arrive at the most efficient use of resources, allowing for a more efficient process.

FIGS. 7-8B illustrate another embodiment in which a multiple channel, multiple gate transistor 800 is formed. In this embodiment, the first channel layer 103 is grown over the first gate dielectric 303, which is already formed and located over the first gate electrode 301. For example, the first channel layer 103 is formed to the first thickness T₁ (less than the critical thickness T_(c)) such that the first channel layer 103 has the properties of a semiconductor material, such as by being less than 6 quintuple layers in an embodiment in which the first channel layer 103 is Bi₂Se₃.

Once the first channel layer 103 has been formed, a first dielectric layer 701 may be formed over the first channel layer 103 in order to separate and isolate the first channel layer 103 (which will become the first channel 305 in the multiple channel, multiple gate transistor 800) from a second channel layer 703 (which will become a second channel 805 in the multiple channel, multiple gate transistor 800). In an embodiment the first dielectric layer 701 may be dielectric material such as aluminum oxide or hafnium oxide that is formed using a process such as ALD, CVD, PVD, combinations of these, or the like. The first dielectric layer 701 may be formed to have an equivalent oxide thickness of between about 0.5 nm and about 2 nm, although any suitable thickness may be utilized.

Once the first dielectric layer 701 has been formed, a second channel layer 703 may be formed on the first dielectric layer 701. In an embodiment the second channel layer 703 will be used to form the second channel 805 of the multiple channel, multiple gate transistor 800 and, as such, may be similar to the first channel layer 103. For example, the second channel layer 703 may be formed from a topological insulator material such as Bi₂Se₃ and may be formed to have the first thickness T₁ which is below the critical thickness T_(c) of the material used for the second channel layer 703. As such, the second channel layer 703 will have the properties of a semiconductor material. In a particular embodiment in which Bi₂Se₃ is used as the material for the second channel layer 703, the second channel layer 703 may be formed to have the first thickness T₁ of less than about six quintuple layers, although any suitable thickness may be utilized.

After the second channel layer 703 has been formed, a second gate dielectric layer 705 is formed over the second channel layer 703. In an embodiment the second gate dielectric layer 705 may be formed from similar materials and using similar processes as the first gate dielectric layer 105 described above with respect to FIG. 1. For example, the second gate dielectric layer 705 may be formed from a dielectric material such as aluminum oxide or hafnium oxide to a thickness of between about 0.5 nm and about 2 nm using a process such as ALD, CVD, PVD, or the like. However, any suitable material or method of manufacturing may be utilized.

Once the second gate dielectric layer 705 has been formed, a second gate electrode layer 707 may be formed over the second gate dielectric layer 705. In an embodiment the second gate electrode layer 707 may be formed from similar materials and using similar processes as the first gate electrode layer 107 described above with respect to FIG. 1. For example, the second gate electrode layer 707 may be formed from a conductive material such as gold, titanium, platinum, aluminum, or the like using a process such as ALD, CVD, PVD, or the like. However, any suitable material or method of manufacturing may be utilized.

FIG. 8A illustrates a formation of the source/drain regions 401. In an embodiment the formation of the source/drain regions 401 may be initiated by first patterning the second gate electrode layer 707 into a second gate electrode 801. In an embodiment the second gate electrode layer 707 is patterned in a similar fashion as the first gate electrode layer 107 was patterned into the first gate electrode 301 (described above with respect to FIG. 3). For example, a photoresist may be placed, exposed, developed, and used as a mask in a photolithographic masking and etching process in order to pattern the second gate electrode layer 707 into the second gate electrode 801. In an embodiment the second gate electrode 801 may be formed to have a sixth width W₆ of between about 7 nm and about 100 μm.

Once the second gate electrode 801 has been formed, the second gate dielectric layer 705, the second channel layer 703, the first dielectric layer 701, and the first channel layer 103 may next be patterned for the eventual formation of the source/drain regions 401. In an embodiment the second gate dielectric layer 705, the second channel layer 703, first dielectric layer 701, and the first channel layer 103 may be patterned by initially placing, exposing, and developing a photoresist over the second gate electrode 801 and exposed second gate dielectric layer 705 and then using the photoresist as a mask during an etching process such as a dry etching process in order to etch through the second gate dielectric layer 705, the second channel layer 703, the first dielectric layer 701, and the first channel layer 103 until the first gate dielectric 303 has been exposed. The patterning will form a second gate dielectric 803 (from the second gate dielectric layer 705), a second channel 805 (from the second channel layer 703) and the first channel 305 (from the first channel layer 103). In an embodiment the second gate dielectric 803, the second channel 805 and the first channel 305 may be formed to have a seventh width W₇ of between about 7 nm and about 100 μm. although any suitable dimension may be utilized.

Once the underlying first gate dielectric 303 has been exposed, the source/drain regions 401 may be formed on opposite sides of the first channel 305 and the second channel 805, and the source/drain regions 401 may be formed as described above with respect to FIG. 4A. For example, the source/drain regions 401 may be formed from the same material as the first channel 305 and the second channel 805 and using an epitaxial growth process to epitaxially grow the source/drain regions 401 onto the exposed first gate dielectric 303. Additionally, the source/drain regions 401, while being grown from the same material as the first channel 305 and the second channel 805, will grow the source/drain regions 401 to have the second thickness T₂ that is at least greater than the critical thickness T_(c) of the material used for the source/drain regions 401 such that the source/drain regions 401 will have the properties of a topological insulator with metallic surface states. For example, in an embodiment in which Bi₂Se₃ is used as the material for the source/drain regions 401, the source/drain regions 401 may be grown to the second thickness T₂ that is greater than six quintuple layers. However, any suitable thickness may be utilized.

FIG. 8B illustrates a top down view of the multiple channel, multiple gate transistor 800. In this embodiment the second gate dielectric 803 may be formed to have a sixth length L₆ of between about 7 nm and about 100 μm. while the second gate electrode 801 may be formed to have a seventh length L₇ of between about 7 nm and about 100 μm. Additionally, the source/drain regions 401 may be formed to have an eighth length L₈ of between about 7 nm and about 100 μm. However, any suitable dimensions may be utilized.

By utilizing the processes described above with respect to FIGS. 7-8B, a multiple channel, multiple gate transistor 800 may be formed. Such a transistor allows for a normally off transistor with the use of topological materials which also has the benefits that multiple channels and multiple gates provide.

In accordance with an embodiment, a method of manufacturing a semiconductor device comprising growing a layer of a first material to a first thickness onto a substrate, the first thickness being less than a critical thickness is provided. A gate dielectric layer and a gate electrode layer are deposited over the layer of the first material and the gate dielectric layer and the gate electrode layer are patterned into a gate stack. The first layer of material is patterned to expose a portion of the substrate, and source/drain regions are grown onto the portion of the substrate, wherein the growing the source/drain regions grows the first material to a thickness greater than the critical thickness.

In accordance with another embodiment, a method of manufacturing a semiconductor device comprising growing a layer of a first material to a first thickness onto a substrate, the first thickness being greater than a critical thickness, is provided. A portion of the first material is removed to form a channel region and an opening over the channel region, wherein the removing the portion of the first material reduces the thickness of at least a portion of the first material to less than the critical thickness and also modifies the properties of the first material within the channel region. A gate dielectric is formed within the opening, and a gate electrode is formed over the gate dielectric.

In accordance with yet another embodiment, a semiconductor device comprising a first channel region comprising a first material, wherein the first material has a critical thickness below which the first material has properties of a semiconductor material and above which the first material has properties of a topological insulator, wherein the first channel region has a first thickness less than the critical thickness is provided. A source/drain region is adjacent to the first channel region, wherein the source/drain region comprises the first material with a second thickness greater than the critical thickness. A gate dielectric is adjacent to the first channel region, and a gate electrode is on an opposite side of the gate dielectric from the first channel region.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

1. A method of manufacturing a semiconductor device, the method comprising: growing a layer of a first material to a first thickness onto a substrate, the first thickness being less than a critical thickness; depositing a gate dielectric layer and a gate electrode layer over the layer of the first material; patterning the gate dielectric layer and the gate electrode layer into a gate stack; patterning the first layer of material to expose a portion of the substrate; and growing source/drain regions onto the portion of the substrate, wherein the growing the source/drain regions grows the first material to a thickness greater than the critical thickness.
 2. The method of claim 1, wherein the growing the layer of the first material is performed at least in part through a first epitaxial growth process.
 3. The method of claim 2, wherein the growing the source/drain regions is performed at least in part through a second epitaxial growth process.
 4. The method of claim 1, wherein the first thickness is less than six quintuple layers.
 5. The method of claim 1, wherein the growing the layer of the first material comprises growing Si₂Be₃.
 6. The method of claim 1, wherein the substrate further comprises: a gate dielectric layer; and a gate electrode layer.
 7. The method of claim 1, further comprising: depositing a first dielectric material onto the layer of the first material prior to the depositing the gate dielectric layer and the gate electrode layer; and growing a second layer of the first material on the first dielectric material prior to the depositing the gate dielectric layer and the gate electrode layer, wherein the patterning the first layer of material further comprises patterning the second layer of the first material.
 8. A method of manufacturing a semiconductor device, the method comprising: growing a layer of a first material to a first thickness onto a substrate, the first thickness being greater than a critical thickness; removing a portion of the first material to form a channel region and an opening over the channel region, wherein the removing the portion of the first material reduces the thickness of at least a portion of the first material to less than the critical thickness and also modifies the properties of the first material within the channel region; and forming a gate dielectric within the opening; forming a gate electrode over the gate dielectric.
 9. The method of claim 8, wherein the growing the layer of the first material is performed at least in part through an epitaxial growth process.
 10. The method of claim 8, wherein the growing the layer of the first material grows Bi₂Se₃.
 11. The method of claim 8, wherein the substrate comprises silicon.
 12. The method of claim 8, wherein the forming the gate dielectric is performed at least in part with an atomic layer deposition process.
 13. The method of claim 8, wherein the forming the gate dielectric is performed at least in part with an atomic layer deposition process. 14.-15. (canceled)
 21. A method of manufacturing a semiconductor device, the method comprising: manufacturing a first channel region comprising a first material, wherein the first material has a critical thickness below which the first material has properties of a semiconductor material and above which the first material has properties of a topological insulator, wherein after the manufacturing the first channel region the first channel region has a first thickness less than the critical thickness; forming a source/drain region adjacent to the first channel region, wherein the source/drain region comprises the first material with a second thickness greater than the critical thickness; forming a gate dielectric; and forming a gate electrode, wherein after the forming the gate electrode, the forming the gate dielectric, and the manufacturing the first channel region the gate electrode is located on an opposite side of the gate dielectric from the first channel region.
 22. The method of claim 21, wherein the forming the gate dielectric forms the gate dielectric with a planar surface facing the first channel region and wherein the source/drain region is formed in physical contact with the planar surface.
 23. The method of claim 21, wherein after the forming the gate dielectric the gate dielectric has a first surface facing the first channel region and a second surface perpendicular to the first surface, wherein the source/drain region is in physical contact with the second surface.
 24. The method of claim 21, further comprising manufacturing a second channel region comprising the first material, wherein the second channel region has a third thickness less than the critical thickness.
 25. The method of claim 24, further comprising depositing a dielectric material after the manufacturing the first channel region and prior to the manufacturing the second channel region.
 26. The method of claim 21, wherein the first material is Bi₂Se₃.
 27. The method of claim 21, wherein the first material is a tetradymite-like ternary compound. 